Recrystallization mechanism of as-cast AZ91 magnesium alloy during hot compressive deformation

Dynamic recrystallization (DRX) behavior of as-cast AZ91 magnesium alloy during hot compression at 300 °C and the strain rate of 0.2 s−1 was systematically investigated by electron backscattering diffraction (EBSD) analysis. Twin DRX and continuous DRX (CDRX) are observed in grains and near grain boundaries, respectively. Original coarse grains are firstly divided by primary {101¯2} tensile twins and {101¯1} compression twins, and then...