Insights into the intergranular corrosion of overlay welded joints of X65-Inconel 625 clad pipe and its relationship to damage penetration

Intergranular corrosion (IGC) behaviors of X65-Inconel 625 clad pipe welded joints of different thickness (1.5, 2.0, 2.5 mm) were investigated. Corrosion tests showed that as the position of the specimen approached to the X65 side, the resistance of IGC decreased. The increased susceptibility of the welded joint to IGC was due to the small grain size and high Fe content. Different corrosion morphologies were observed in the base metal (BM) and...