High-temperature corrosion performance of HVAF-sprayed NiCr, NiAl, and NiCrAlY coatings with alkali sulfate/chloride exposed to ambient air

The high-temperature corrosion of high velocity air-fuel (HVAF) thermal spray Ni21Cr, Ni5Al, and Ni21Cr7AlY coatings was investigated at 600 °C for 168 h in ambient air under KCl and 50-50 mol% KCl–K2SO4 salts. Chlorination-oxidation cycle and breakdown of the corrosion products layer were the dominant corrosion mechanism in the chromia-forming Ni21Cr and Ni21Cr7AlY coatings exposed to KCl. KCl–K2SO4 was less corrosive to the chromia-forming...