Internal oxidation of Alloy 600 exposed to hydrogenated steam and the beneficial effects of thermal treatment

Alloy 600 in the solution annealed (SA) and thermally treated (TT) conditions was exposed to a hydrogenated steam environment considered to simulate primary water in pressurized water reactors. The likely susceptibility to primary water stress corrosion cracking (PWSCC) was evaluated using the internal oxidation model. A FIB was used to extract cross-sections from Alloy 600 samples and elemental maps were generated; internal oxidation was...